As a elastomer, TPU is a kind of medium material between rubber and plastic, looking at its rigidity,measured by elasticity modulus, rubber is normally 1-10Mpa, TPU is 10-1000Mpa,plastic (PA, ABS, PC, POM) is 1000~10000Mpa. TPU has a wide range of hardness from Shore A 60 to Shore D 80, still has high elasticity; in a wide temperature range of-40-120℃ , TPU is still pliable, no need to add plasticizer; good resistance to oil( mineral oil, lubricant oil, animal and vegetable oil) and many solvents; either good resistance to weather, excellent resistance to high-energy ray; well-known abrasive resistance, tear resistance and yield strength are admirable; high tensile strength, big elongation, long-term compression permanent deformation rate is either low.

Fat Group TPU-DH Series
Product characters：Aliphatic, no discoloration, fine water resistant, fine cold resistant, quick mold release, easy processing flexible on low temperature, etc
Application field：no discoloration materials.

Physical Character	Unit	Detection method	DH60A	DH65A	DH70A	DH75A	DH80A	DH85A	DH90A
Hardness	Shore A/D	ASTM D2240	60A ± 2	65A ± 2	70A ± 2	75A ± 2	80A ± 2	85A ± 2	90A ± 2
Density	g/cm3	ASTM D792	1.02	1.02	1.03	1.03	1.04	1.04	1.05
Tensile Strength	kg/cm2	ASTM D412	190	230	290	360	400	460	510
Elongation	%	ASTM D412	600	560	520	460	430	390	350
100% Modulus	kg/cm2	ASTM D412	60	70	80	90	120	160	180
300% Modulus	kg/cm2	ASTM D412	180	210	230	280	360	405	450
Tearing Strength	kg/cm	ASTM D624	65	72	78	83	90	95	110
Abrasion	mm3	DIN 53516	70	65	60	55	50	60	65
Manufacturing Advice	Drying Condition (°Cxhrs)		100*3	100*3	100*3	100*3	100*3	100*3	100*3
Manufacturing Advice	Manufacturing Temperature （℃）		160-170	165-175	165-175	170-180	170-180	175-185	175-185

All abovementioned anti-yellowing index reach level 3.0, also could be customized according to the special demands from the customers
Abovementioneed data are the averaged va1ue after lots of testing,pls take as reference

Chemistry Praise The Virtues Of Life
Along With The New Materials And Technology Being Developed And Improved, In The Future We Believe Oss Will Create A High Quality Life For You.

THAnk You For Your Attention To OSS!
As a elastomer, TPU is a kind of medium material between rubber and plastic, looking at its rigidity,measured by elasticity modulus, rubber is normally 1-10Mpa, TPU is 10-1000Mpa,plastic (PA, ABS, PC, POM) is 1000~10000Mpa. TPU HAs a wide range of HArdness from Shore A 60 to Shore D 80, still HAs high elasticity; in a wide temperature range of-40-120℃ , TPU is still pliable, no need to add plasticizer; good resistance to oil( mineral oil, lubricant oil, animal and vegetable oil) and many solvents; either good resistance to weather, excellent resistance to high- energy ray; well-known abrasive resistance, tear resistance and yield strength are admirable; high Tensile
Strength, big elongation, long-term compression permanent deformation rate is either low.

Fat Group TPU-DH Series
Product cHAracters：Aliphatic, no discoloration, fine water resistant, fine cold resistant, quick mold release, easy processing flexible on low temperature, etc
Application field：no discoloration materials.

Physical CHAracter	Unit	Detection method	DH60A	DH65A	DH70A	DH75A
HArdness	Shore A/D	ASTM D2240	60A ± 2	65A ± 2	70A ± 2	75A ± 2
			DH80A	DH85A	DH90A	/
			80A ± 2	85A ± 2	90A ± 2	/
Density	g/cm3	ASTM D792	DH60A	DH65A	DH70A	DH75A
			1.02	1.02	1.03	1.03
			DH80A	DH85A	DH90A	/
			1.04	1.04	1.05	/
Tensile Strength	kg/cm2	ASTM D412	DH60A	DH65A	DH70A	DH75A
			190	230	290	360
			DH80A	DH85A	DH90A	/
			400	460	510	/
Elongation	%	ASTM D412	DH60A	DH65A	DH70A	DH75A
			600	560	520	460
			DH80A	DH85A	DH90A	/
			430	390	350	/
100% Modulus	kg/cm2	ASTM D412	DH60A	DH65A	DH70A	DH75A
			60	70	80	90
			DH80A	DH85A	DH90A	/
			120	160	180	/
300% Modulus	kg/cm2	ASTM D412	DH60A	DH65A	DH70A	DH75A
			180	210	230	280
			DH80A	DH85A	DH90A	/
			360	405	450	/
Tearing Strength	kg/cm	ASTM D624	DH60A	DH65A	DH70A	DH75A
			65	72	78	83
			DH80A	DH85A	DH90A	/
			90	95	110	/
Abrasion	mm3	DIN 53516	DH60A	DH65A	DH70A	DH75A
			70	65	60	55
			DH80A	DH85A	DH90A	/
			50	60	65	/
Manufacturing Advice	Drying Condition （℃*hrs）		DH60A	DH65A	DH70A	DH75A
			100*3	100*3	100*3	100*3
			160-170	165-175	165-175	170-180
	Manufacturing Temperature （℃）		DH80A	DH85A	DH90A	/
			100*3	100*3	100*3	/
			170-180	175-185	175-185	/