As a elastomer, TPU is a kind of medium material between rubber and plastic, looking at its rigidity,measured by elasticity modulus, rubber is normally 1-10Mpa, TPU is 10-1000Mpa,plastic (PA, ABS, PC, POM) is 1000~10000Mpa. TPU has a wide range of hardness from Shore A 60 to Shore D 80, still has high elasticity; in a wide temperature range of-40-120℃ , TPU is still pliable, no need to add plasticizer; good resistance to oil( mineral oil, lubricant oil, animal and vegetable oil) and many solvents; either good resistance to weather, excellent resistance to high-energy ray; well-known abrasive resistance, tear resistance and yield strength are admirable; high tensile strength, big elongation, long-term compression permanent deformation rate is either low.

Polyester TPU-HT Series
Product characters：high transparency, good fluidity, fast-molding, anti-hydrolytic, anti-yellowing, applicable to transparent injection molding with 6mm wall thickness.
Application field：shoe materials, sheets, shoulder belt, truckle and transparent ornaments.

Physical Character	Unit	Detection method	HT85A	HT90A	HT95A	HT98A	HT64D	HT72D	HT80D
Hardness	Shore A/D	ASTM D2240	85A ± 2	90A ± 2	95A ± 2	98A ± 2	64D ± 2	72D ± 2	80D ± 2
Density	g/cm3	ASTM D792	1.19	1.19	1.20	1.21	1.21	1.22	1.23
Tensile Strength	kg/cm2	ASTM D412	300	350	400	460	550	600	650
Elongation	%	ASTM D412	580	520	490	450	400	310	300
100% Modulus	kg/cm2	ASTM D412	65	95	150	170	210	250	290
300% Modulus	kg/cm2	ASTM D412	150	250	310	390	450	540	610
Tearing Strength	kg/cm	ASTM D624	106	160	180	200	210	250	280
Abrasion	mm3	DIN 53516	43	43	47	50	55	55	60
Manufacturing Advice	Drying Condition (°Cxhrs)		100*3	105*3	105*3-5	105*3-5	105*3-5	105*3-5	105*3-5
Manufacturing Advice	Manufacturing Temperature （℃）		175-185	180-190	185-195	185-195	190-200	195-205	200-210

All abovementioned anti-yellowing index reach level 3.0, also could be customized according to the special demands from the customers
Abovementioneed data are the averaged va1ue after lots of testing,pls take as reference

Chemistry Praise The Virtues Of Life
Along With The New Materials And Technology Being Developed And Improved, In The Future We Believe Oss Will Create A High Quality Life For You.

THAnk You For Your Attention To OSS!
As a elastomer, TPU is a kind of medium material between rubber and plastic, looking at its rigidity,measured by elasticity modulus, rubber is normally 1-10Mpa, TPU is 10-1000Mpa,plastic (PA, ABS, PC, POM) is 1000~10000Mpa. TPU HAs a wide range of HArdness from Shore A 60 to Shore D 80, still HAs high elasticity; in a wide temperature range of-40-120℃ , TPU is still pliable, no need to add plasticizer; good resistance to oil( mineral oil, lubricant oil, animal and vegetable oil) and many solvents; either good resistance to weather, excellent resistance to high- energy ray; well-known abrasive resistance, tear resistance and yield strength are admirable; high Tensile
Strength, big elongation, long-term compression permanent deformation rate is either low.

Polyester TPU-HT Series
Product cHAracters：high transparency, good fluidity, fast-molding, anti-hydrolytic, anti-yellowing, applicable to transparent injection molding with 6mm wall thickness.
Application field：shoe materials, sheets, shoulder belt, truckle and transparent ornaments.

Physical CHAracter	Unit	Detection method	HT85A	HT90A	HT95A	HT98A
HArdness	Shore A/D	ASTM D2240	85A±2	90A±2	95A±2	98A±2
			HT64D	HT72D	HT80D	/
			64A±2	72A±2	80A±2	/
Density	g/cm3	ASTM D792	HT85A	HT90A	HT95A	HT98A
			1.19	1.19	1.2	1.21
			HT64D	HT72D	HT80D	/
			1.21	1.22	1.23	/
Tensile Strength	kg/cm2	ASTM D412	HT85A	HT90A	HT95A	HT98A
			300	350	400	460
			HT64D	HT72D	HT80D	/
			550	600	650	/
Elongation	%	ASTM D412	HT85A	HT90A	HT95A	HT98A
			580	520	490	450
			HT64D	HT72D	HT80D	/
			400	310	300	/
100% Modulus	kg/cm2	ASTM D412	HT85A	HT90A	HT95A	HT98A
			65	95	150	170
			HT64D	HT72D	HT80D	/
			210	250	290	/
300% Modulus	kg/cm2	ASTM D412	HT85A	HT90A	HT95A	HT98A
			150	250	310	390
			HT64D	HT72D	HT80D	/
			450	540	610	/
Tearing Strength	kg/cm	ASTM D624	HT85A	HT90A	HT95A	HT98A
			106	160	180	200
			HT64D	HT72D	HT80D	/
			210	250	280	/
Abrasion	mm3	DIN 53516	HT85A	HT90A	HT95A	HT98A
			43	43	47	50
			HT64D	HT72D	HT80D	/
			55	55	60	/
Manufacturing Advice	Drying Condition （℃*hrs）		HT85A	HT90A	HT95A	HT98A
			100*3	105*3	105*3-5	105*3-5
			175-185	180-190	185-195	185-195
	Manufacturing Temperature （℃）		HT64D	HT72D	HT80D	/
			105*3-5	105*3-5	105*3-5	/
			190-200	195-205	200-210	/